High cycle fatigue of bearing steel

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F04%3A00108346" target="_blank" >RIV/68081723:_____/04:00108346 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
High cycle fatigue of bearing steel
Original language description
S-N curve of 14109 bearing steel was experimentally determined in symmetrical tension-compression in the interval of 10 to 5 to 10 to 8 cycles to fracture. Continuous increase of the number of cycles to fracture with decreasing stress amplitude was observed. Large scatter of experimental data is related to the initiation of fatigue cracks on internal defects of Al2O3 and TiN type.
Czech name
Vysokocyklová únava ložiskové oceli
Czech description
Experimentálně byla stanovena S-N křivka ložiskové oceli 14109 při zatěžování v symetrickém tahu-tlaku v intervalu od 10 na patou do 10 na osmou cyklů. S klesající amplitudou napětí byl pozorován spojitý růst únavové životnosti. Velký rozptyl experimentálních hodnot je spojen s iniciací únavových trhlin na vnitřních defektech typu Al2O3 a TiN.

Project
<a href="/en/project/IBS2041001" target="_blank" >IBS2041001: Degradation of properties and lifetime assessment of engineering materials under mechanical loading</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Publication year
2004
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)