Bulk and grain boundary diffusion of 67Ga in Ni3Al - influence of composition
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F05%3A00108284" target="_blank" >RIV/68081723:_____/05:00108284 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—
Alternative languages
Result language
angličtina
Original language name
Bulk and grain boundary diffusion of 67Ga in Ni3Al - influence of composition
Original language description
The effect of composition and temperature on the 67Ga bulk and GB diffusion was studied in the binary Ni-rich Ni3Al alloys in the temperature range of 773 - 1373 K. The compositions of alloys were 22.4, 23.8 and 24.8 at.% Al. In accordance with the related results in the literature, it was found that both bulk and GB diffusivity increased with decreasing Al content in the concentration interval studied
Czech name
Objemová difúze 67Ga a difúze 67Ga podél hranic zrn v NI3Al - vliv složení
Czech description
Vliv chemického složení a teploty na objemovou difúzi 67Ga a difúzi 67Ga podél hranic zrn byla studován v binárních niklem bohatých slitinách Ni3Al v teplotním rozsahu 773 - 1373 K. Chemické složení slitin bylo 22,4; 23,8 a 24,8 at.% Al. V souladu s příbuznými literárními výsledky, bylo zjištěno, že objemová difúze a difúze podél hranic zrn se zvyšuje se snižujícím se obsahem Al ve studovaném koncentračním rozsahu
Classification
Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
BM - Solid-state physics and magnetism
OECD FORD branch
—
Result continuities
Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)
Others
Publication year
2005
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Name of the periodical
Intermetallics
ISSN
0966-9795
e-ISSN
—
Volume of the periodical
13
Issue of the periodical within the volume
1
Country of publishing house
NL - THE KINGDOM OF THE NETHERLANDS
Number of pages
8
Pages from-to
113-120
UT code for WoS article
—
EID of the result in the Scopus database
—