Fatigue behaviour of ultrafine-grained copper
Original language description
Mechanical properties and fatigue behaviour of ultrafine-grained materials during cyclic loading are not well described and understood. The paper presents experimental results on fatigue lifetime and cyclic plastic properties of ultrafine-grained copperprepared by equal channel angular pressing. It has been observed that fatigue loading did not result in a substantial change of ultraafine-grained microstructure. In spite of this the cyclic stress-strain response changes qualitatively in dependence on the stress amplitude.
Czech name
Únavové chování ultrajemnozrnné mědi
Czech description
Mechanické vlastnosti a únavové chování ultrajemnozrnných materiálů nejsou doposud dostatečně dobře popsány a pochopeny. Příspěvek presentuje experimentální výsledky popisujcící únavovou životnost a cyklické plastické vlastnosti ultrajemnozrnné Cu připravené intenzivní plastickou deformací. Bylo zjištěno, že únavové zatěžování nezpůsobuje podstatné změny v ultrajemnozrnné struktuře. Na druhé straně napěťově-deformační odezva se kvalitativně mění v závislsti na amplitudě napětí.

Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
Z - Vyzkumny zamer (s odkazem do CEZ)

Publication year
2007
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)