Microstructure evolution of an Al-Pd-Co alloy

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F08%3A00313591" target="_blank" >RIV/68081723:_____/08:00313591 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Microstructure evolution of an Al-Pd-Co alloy
Original language description
A complex metallic alloy of the nominal chemical composition of 73.5Al-11Pd-15.5Co (at.%)was annealed at 1000 oC for 92 hours and then investigated with light microscopy, differnential thermal analysis, scanning electron microscopy including energy and wavelenght dispersive X-ray spectrocsopy, and X-ray diffraction. Were found the ternary U-phase, binary ?-phase, and non-identified phase.
Czech name
Vývoj mikrostruktury slitiny Al-Pd-Co
Czech description
Komplexní slitina nominálního chemického složení 73.5Al-11Pd-15.5Co (at.%) byla žíhána za teploty 1000 oC po dobu 92 hodin a pak zkoumána pomocí světelné mikroskopie, DTA, SEM včetně energ. a vlnově disperzní rtg. analýzy. Byly nalezeny ternární U-fáze,binární ?-fáze a neidentifikovaná fáze.

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JG - Metallurgy, metal materials
OECD FORD branch
—

Project
<a href="/en/project/GA106%2F07%2F1259" target="_blank" >GA106/07/1259: Quasicrystalline phases in the Al-Pd-TM system</a><br>
Continuities
Z - Vyzkumny zamer (s odkazem do CEZ)

Publication year
2008
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)