Micromechanisms and Micromechanics of Fracture of TiAl Intermetallics
Original language description
The paper is focused on the analysis of the role of microstructure in fracture performance of TiAl intermetalics at room and elevated temperatures. Tensile properties, flexural strength and fracture toughness have been evaluated for Ti-40Al-2Cr-2Nb-1B and Ti-46Al-0,7Cr-0,1Si-7Nb-0,2Ni alloys. Positive Nb effect on fracture resistance was found; fracture toughness of the high Nb alloy was increased at contemporary increase of tensile and flexural strength. Fracture surfaces were evaluated using scanningelectron microscopy showing the key role of mechanical twinning in deformation of both alloys. As a governing mechanism of the crack initiation a microcrack nucleation at boundaries between deformation twins and -TiAl grains was confirmed. Extensive development of shear ligament toughening was observed supplying quite good fracture toughness values in high Nb alloy. Based on findings obtained key aspects of the effect of separate microstructural components have been discussed.
Czech name
—
Czech description
—

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JG - Metallurgy, metal materials
OECD FORD branch
—

Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
Z - Vyzkumny zamer (s odkazem do CEZ)

Publication year
2009
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)