High-temperature long-service embrittlement of the R.A.F.M. EUROFER´97 steel

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F09%3A00332730" target="_blank" >RIV/68081723:_____/09:00332730 - isvavai.cz</a>
Alternative codes found
RIV/00216305:26210/09:PU87800
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
High-temperature long-service embrittlement of the R.A.F.M. EUROFER´97 steel
Original language description
The ferritic-martensitic reduced activation steel Eurofer´97 is candidate structural material for in-vessel components of proposed fusion reactors. The embrittlement of the high-chromium ferritic-martensitic steels implies important limitation for use ofthese materials. The microstructure and fracture properties of the Eurofer´97 steel sheets of thickness 25 mm were investigated in as-received state and in state after long-time thermal ageing (550 °C/5.000 h/air). Detailed microstructure studies were carried out by means of optical, electron and quantitative electron microscopy in as-received state and in state after long-time thermal ageing. Mechanical properties were evaluated in both states by means of Charpy impact testing. The microstructure of the Eurofer´97 consisted of tempered martensite with M23C6 and MX precipitates. The isothermal ageing caused evident shift in tDBTT about +5 °C, no proofs of embrittlement were observed on fracture surfaces.
Czech name
—
Czech description
—

Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Publication year
2009
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)