High-cycle fatigue of Ni-base superalloy Inconel 713LC

Result code in IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F10%3A00353410" target="_blank" >RIV/68081723:_____/10:00353410 - isvavai.cz</a>

Result on the web

—

DOI - Digital Object Identifier

—

Result language

angličtina

Original language name

High-cycle fatigue of Ni-base superalloy Inconel 713LC

Original language description

Fatigue strength of three nominally identical batches of cast Ni-base superalloy INCONEL 713LC under load symmetrical cycling and cycling with tensile mean load was experimentally determined in high-cycle fatigue region at a temperature of 800 °C in air.Examination of fracture surfaces, crack initiation sites, microstructure and casting defects has been performed. Statistical method of largest extreme value distribution has been applied to characterize the casting defect distribution. The aim of the study was to evaluate the mean stress effect on high-cycle fatigue life, to explain the scatter of fatigue life data and a scatter related to material produced under nominally identical production conditions.

Czech name

—

Czech description

—

Type

J_x - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)

CEP classification

JL - Fatigue and fracture mechanics

OECD FORD branch

—

Project

Result was created during the realization of more than one project. More information in the Projects tab.

Continuities

Z - Vyzkumny zamer (s odkazem do CEZ)

Publication year

2010

Confidentiality

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Name of the periodical

International Journal of Fatigue

ISSN

0142-1123

e-ISSN

—

Volume of the periodical

32

Issue of the periodical within the volume

6

Country of publishing house

GB - UNITED KINGDOM

Number of pages

6

Pages from-to

—

UT code for WoS article

000275890000007

EID of the result in the Scopus database

—