Combined Cycle Fatigue of Ni-Base Superalloy

Result code in IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F11%3A00358394" target="_blank" >RIV/68081723:_____/11:00358394 - isvavai.cz</a>

Result on the web

—

DOI - Digital Object Identifier

—

Result language

angličtina

Original language name

Combined Cycle Fatigue of Ni-Base Superalloy

Original language description

Fatigue life of a cast Ni-base superalloy IN 713LC under combined cycle loading consisting of a superposition of low- and high-cycle fatigue at 800 °C was experimentally determined. No measurable effect of combined cycle was found for studied loading conditions. High scatter of fatigue life related to the initiation of cracks on casting defects was observed. Size of the largest defect in a specimen was predicted by the largest extreme value distribution method. The predicted size was compared with fractographic observation of defects resulting in final fatigue failure.

Czech name

—

Czech description

—

Type

J_x - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)

CEP classification

JL - Fatigue and fracture mechanics

OECD FORD branch

—

Project

<a href="/en/project/FT-TA4%2F023" target="_blank" >FT-TA4/023: Research and development of mechanical properties of the materials used for new types of turbochargers. and development of a new, more advanced technology of precision casting of impeller wheels of the developed turbochargers.</a><br>

Continuities

Z - Vyzkumny zamer (s odkazem do CEZ)

Publication year

2011

Confidentiality

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Name of the periodical

Key Engineering Materials

ISSN

1013-9826

e-ISSN

—

Volume of the periodical

2011

Issue of the periodical within the volume

465

Country of publishing house

CH - SWITZERLAND

Number of pages

4

Pages from-to

523-526

UT code for WoS article

—

EID of the result in the Scopus database

—