HIGH - TEMPERATURE CREEP BEHAVIOUR OF CAST COBALT-BASE SUPERALLOYS

Original language description

Two cast and heat-treated NbC and TaC – strengthened cobalt superalloys have been developed for a precision casting of spinner discs for glass wool industry. In this work constant load creep tests in tension were carried out in argon atmosphere at three testing temperature 900, 950 and 1000 °C and at the initial applied stresses ranged from 40 to 200 MPa. All the tests were continued until the final fracture. The results of creep testing were combined with microstructural and fractographic examinations by means of light and scanning electron microscopy. A mutual comparison of creep characteristics of the investigated superalloys under comparable creep loading conditions showed that NbC-strengthened superalloy exhibited longer creep life than TaC-strengthened one. Further, it was found that carbide precipitation is the primary strengthening mechanism in both cobalt-base superalloys under investigation and the amount, morphologynand type of carbides have the decisive effect on the creep properties including creep damage and fracture processes. By contrast, NbC-superalloy exhibited a more brittle character of creep fracture mode than TaCstrengthened superalloy. This study was initiated to investigate in more details creep deformation processes and the effect of the creep microstructure and damage evolution on both investigated superalloys. The different behaviour and properties of studied superalloys were explained based on the received results of this study.

Czech name

—

Czech description

—

Type

D - Article in proceedings

CEP classification

—

OECD FORD branch

20501 - Materials engineering

Project

Result was created during the realization of more than one project. More information in the Projects tab.

Continuities

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year

2018

Confidentiality

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Article name in the collection

Metal 2018 - 27th International conference on metallurgy and materials, Conference Proceedings

ISBN

978-80-87294-84-0

ISSN

—

e-ISSN

—

Number of pages

6

Pages from-to

530-535

Publisher name

TANGER Ltd

Place of publication

Ostrava

Event location

Brno

Event date

May 23, 2018

Type of event by nationality

WRD - Celosvětová akce

UT code for WoS article

000461832200080