Dielectric tunability of SrTiO3 thin films in the terahertz range

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F06%3A00076355" target="_blank" >RIV/68378271:_____/06:00076355 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Dielectric tunability of SrTiO3 thin films in the terahertz range
Original language description
We determined the electric field dependence of the complex permitivity of SrTiO3 thin film on a sapphire substrate up to about 2 THz employing time-domain terahertz spectroscopy. We have demonstrated up to 10% variation of the film permitivity at 300 GHzat room temperature induced by an applied electric field of 100 kV/cm. The field-induced changes are attributed to soft mode hardening
Czech name
Dielektrická laditelnost tenkých vrstev SrTiO3 v terahertzové oblasti
Czech description
Určili jsme závislost komplexní permitivity epitaxní tenké vrystvy SrTiO3 na přiloženém elektrickém poli pomocí terahertzové spektroskopie v časové oblasti. Změřili jsme 10% změnu dielektrické konstanty vrstvy při pokojové teplotě u 300 GHz a při přiloženém poli 100 kV/cm. Mezi 1 MHz a 500 GHu nebyla pozorována žádná disperze. Tyto jevy byly přisouzeny tvrdnutí měkkého módu

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
BM - Solid-state physics and magnetism
OECD FORD branch
—

Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Publication year
2006
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)