Needle-like domain structure in Co films deposited on Mo (1 1 0)
Original language description
Magnetization reversal processes and domain structures have been studied in Mo(110)/Co(0001)/Au(111) structures grown by molecular beam epitaxy on monocrystalline (1120) sapphire substrates. Wedge-shaped samples with different Co thickness gradients relative to the Mo [001] direction were fabricated. Observation of the domain structure was performed at room temperature using Kerr microscopy in a Co thickness range varying from 5 to 50 nm, where the magnetization is oriented in the plane of the sample.
Czech name
Jehle-podobná doménová struktura ve vrstvách Co napařených na Mo (101)
Czech description
Byl zkoumán proces přemagnetování a doménové struktury v Mo(110)/Co(0001)/Au(111) strukturách vzrostlých pomocí molekulární epitaxe na monokrystalické safírové podložce. Rozborem pozice doménové stěny během přemagnetování se objevila závislost koercitivní síly od tloušťky kobaltové vrstvy. Orientace a průměr jehle podobných domén záleží od tlouštky Co vrstvy a orientace magnetického pole.

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
BM - Solid-state physics and magnetism
OECD FORD branch
—

Publication year
2007
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)