Non-destructive Observation of Damage Processes in Loaded High Ductile Specimens with Different Crack Configuration by X-Ray Dynamic Defectoscopy

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378297%3A_____%2F05%3A00028103" target="_blank" >RIV/68378297:_____/05:00028103 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Non-destructive Observation of Damage Processes in Loaded High Ductile Specimens with Different Crack Configuration by X-Ray Dynamic Defectoscopy
Original language description
This work reports on the results of the experimental observation of development and evolution of material damage during loading processes in aluminium alloy flat specimens. The dependence of intensity and shape of damage zone on the crack configuration,previously little investigated experimentally, has been determined.
Czech name
Nedestruktivní pozorování poškozujících procesů v zatěžovaných, vysoce plastizujících vzorcích, s různými konfiguracemi trhliny X-ray dynamickou defektoskopii
Czech description
Práce představuje výsledky z experimentálního pozorování vzniku a rozvoje poškození materiálu v plochém vzorku z hliníkové slitiny během zatěžovacího procesu. Byla určena dosud málo experimentálně prozkoumaná závislost intenzity a tvaru zóny poškození nakonfiguraci trhliny.

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JL - Fatigue and fracture mechanics
OECD FORD branch
—

Project
<a href="/en/project/GA106%2F00%2FD064" target="_blank" >GA106/00/D064: Experimental investigation of the damage in ductile materials by voids evolution using an X-ray and fast position sensitive pixel detector system</a><br>
Continuities
Z - Vyzkumny zamer (s odkazem do CEZ)

Publication year
2005
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)