Effect of Elevated Temperature on Texture, Composition and Properties of Fiber Reinforced Cement Composites

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21110%2F08%3A01150143" target="_blank" >RIV/68407700:21110/08:01150143 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Effect of Elevated Temperature on Texture, Composition and Properties of Fiber Reinforced Cement Composites
Original language description
Behavior of four types of fiber reinforced cement based composites was studied after thermal load up to 1000° C. As the reinforcement were used glass and PP fibers, PVA fibers, aramid fibers and carbon fibers. It was found that three independent degradation process take place when the composites are thermally loaded. The effect of thermally unstable fibers (PVA, aramid) on moisture diffusivity is less important than effect of the cement matrix thermal degradation.
Czech name
Vliv zvýšené teploty na texturu, složení a vlastnosti cementových kompozitů s vláknovou výztuží
Czech description
Vlastnosti čtyř typů cementových kompozitů s vláknovou výztuží byly studovány po teplotním zatížení do 1000° C. Skleněná, polypropylenová, PVA a aramidová vlákna byla využita jako rozptýlená výztuž. Bylo ukázáno, že v kompozitech po teplotním zatížení probíhají tři nezávislé degradační procesy. Vliv teplotně nestabilních vláken (PVA, aramid) na součinitel vlhkostní vodivosti je méně významný než vliv teplotní degradace cementové matrice.