Investigation of Sintering in Electroceramics by Thermodilatometry

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21110%2F13%3A00205944" target="_blank" >RIV/68407700:21110/13:00205944 - isvavai.cz</a>
Result on the web
<a href="http://dx.doi.org/10.2298/SOS1301003T" target="_blank" >http://dx.doi.org/10.2298/SOS1301003T</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.2298/SOS1301003T" target="_blank" >10.2298/SOS1301003T</a>

Result language
angličtina
Original language name
Investigation of Sintering in Electroceramics by Thermodilatometry
Original language description
Solid-state sintering was investigated in electroceramic samples using thermodilatometric measurements. The samples were studied in the isothermal regime at the temperatures 500, 600, 700, 800, 900, 1000 and 1050 °C. The relative expansion was measured for a period of 8 h. At a given temperature a dominant diffusion mechanism for the sintering process was determined, and the corresponding porosity together with the pore size distribution was also measured.
Czech name
—
Czech description
—

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JH - Ceramics, fire-proof materials and glass
OECD FORD branch
—

Project
<a href="/en/project/GBP105%2F12%2FG059" target="_blank" >GBP105/12/G059: Cumulative time dependent processes in building materials and structures</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2013
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)