Tribological Characteristics of Duplex Treated High-Speed Steels

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21220%2F04%3A02103461" target="_blank" >RIV/68407700:21220/04:02103461 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Tribological Characteristics of Duplex Treated High-Speed Steels
Original language description
The high speed steel M2 made by powder metallurgy was plasma nitrided and duplex-coated at various combinations of processing parameters. The wear resistance of non-nitrided, PVD-coated and duplex-coated steel surface was examined by the ring-on-plate, plate-on-plate and crossed-cylinder tribological testers. The optimal conditions of the plasma nitriding from the point of view of the wear resistance were established. Effect of subsequent PVD-coating realised on plasma nitrided specimens can be considered as very positive when the specimens were heavily loaded
Czech name
Tribologické charakteristiky duplexně zpracovaných rychlořezných ocelí
Czech description
Rychlořezná ocel M2, vyrobená práškovou metalurgií, byla plasmově nitridována a duplexně povlakována různými kombinacemi parametrů procesu. Otěruvzornost nenitridované, PVD-povlakované a duplexně povlakované oceli byla vyšetřována testy pomocí testů ring-on-plate, plate-on-plate a zkříženými válci. Optimální podmínky plasmové nitridace s ohledem na otěruvzdornost byly nalezeny. Vliv následného PVD -povlakování na plasmově nitridovaných vzorcích lze považovat za velmi pozitivní, zejména když jsou vzorkyzatěžovány velkými silami.