Surface Processing of the PM Vanadis 6 Steel with Plasma Nitriding and CrN PVD - Coating

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21220%2F07%3A02136832" target="_blank" >RIV/68407700:21220/07:02136832 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Surface Processing of the PM Vanadis 6 Steel with Plasma Nitriding and CrN PVD - Coating
Original language description
The effect of duplex coating with the combination of PVD CrN and plasma nitriding on the structure and wear resistance of PM Vanadis 6 steel was investigated. The sequence of the nitride formation due the plasma nitriding and its effect on main properties of the steel as well as on the adhesion of PVD-layers was determined. Pre-nitrided as well as un-nitrided steel was PVD-coated with the CrN. The beneficial effect of the pre - nitriding on the adhesion and wear resistance of coated materials is clearlyshown, particularly for the heavily loaded specimens. This is closely connected with the supporting effect of harder nitrided inter - layer.
Czech name
Povrchové zpracování oceli Vanadis 6 plasmovou nitridací a povlakováním vrstvou PVD CrN
Czech description
Byl analyzován vliv duplexního povlakování (kombinace plasmové nitridace a PVD CrN) na strukturu a otěruvzdornost PM oceli Vanadis 6. Zjištěna byla postupnost tvorby nitridů a její vliv na hlavní vlastnosti oceli a stejně tak na adhezi PVD-vrstev. Bylo zjištěno, že plasmová nitridace má příznivý vliv na adhezi a otěruvzdornost povlakovaného materiálu, zejména v případě vysokého zatížení vzorků. Tato skutečnost je přímo ovlivněna zpevňujícím účinkem tvrdé nitridované mezivrstvy.