The Interaction of Natural Ageing with Straining in a Twin-roll Cast AlMgSi Automotive Sheet

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21340%2F06%3A04121732" target="_blank" >RIV/68407700:21340/06:04121732 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
The Interaction of Natural Ageing with Straining in a Twin-roll Cast AlMgSi Automotive Sheet
Original language description
Straining, whether employed shortly after or long after the solution treatment, produces a favorable effect on the T8X strength of a twin-roll cast AlMgSi automotive sheet. Clustering is largely suppressed when sheet samples are strained before natural ageing. Clusters, already present when the sheet samples are strained after natural ageing, transform to stable Guinier–Preston GP-1 zones during the paint-bake.
Czech name
Interakce přirozeného stárnutí a plastické deformace plynule litých pásů ze slitiny AlMgSi pro automobilové aplikace
Czech description
Plastická deformace aplikovaná krátce nebo po delší době po rozpouštěcím žíhání má pozitivní efekt na pevnost plynule litých pásů ze slitiny AlMgSi ve stavu T8X. Je-li materiál deformován před přirozeným stárnutím, tvorba shluků příměsových atomů je výrazně omezena. V materiálu deformovaném po přirozeném stárnutí se tyto shluky transformují na stabilní zóny GP1.

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JG - Metallurgy, metal materials
OECD FORD branch
—

Publication year
2006
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)