Fracture Behaviour of Fe3Al Based Alloys with Cr and Zr Addition

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21340%2F07%3A04134975" target="_blank" >RIV/68407700:21340/07:04134975 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Fracture Behaviour of Fe3Al Based Alloys with Cr and Zr Addition
Original language description
This paper presents a study of fracture behaviour of two Fe3Al based intermetallic alloys with different Zr content - 0.2 and 0.6 at%. The main fracture micromechanism is transgranular cleavage and it does not change significantly with increasing temperature. The fracture mechanism under dynamic loading practically did not change during the transformation D03 <-> B2. On the other hand under static loading, after the transformation D03 <-> B2 transgranular cleavage changes to ductile dimpled fracture.
Czech name
Lomové chování slitin na bázi Fe3Al legovaných Cr a Zr
Czech description
Článek se zabývá lomovým chováním dvou slitin na bázi intermetalika Fe3Al s různým obsahem Zr - 0.2 a 0.6 at%. Hlavním mikromechanismem lomu je transkrystalické štěpení, a to bez výrazné změny se zvyšující se teplotou. Při dynamickém zatěžování se mechanismus lomu prakticky nezměnil ani po transformaci D03 <-> B2. Naproti tomu při statickém zatěžování se po transformaci D03 <-> B2 transkrystalický štěpný lom mění na tvárný důlkový lom.