Influence of Environment and Loading on Failure Processes of Stainless Steel AISI 304L

Result code in IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21340%2F09%3A00160374" target="_blank" >RIV/68407700:21340/09:00160374 - isvavai.cz</a>

Result on the web

—

DOI - Digital Object Identifier

—

Result language

angličtina

Original language name

Influence of Environment and Loading on Failure Processes of Stainless Steel AISI 304L

Original language description

A wide experimental programme is realised in Joint Research Centre, Institute for Energy Petten in the frame of project SAFELIFE. One part of this programme is focused on the study of stress corrosion cracking (SCC) resistance of materials for WWER and PWR core internals materials in simulated reactor conditions by means of slow J-R and standard SCC tests. Stress corrosion cracking tests (SCC) of AISI 304L stainless steel with different degree of cold working has been carried out under BWR condition. Inthe frame of this research fractographic laboratory of Department of Materials FNSPE CTU in Prague was asked to carry out fractographic analysis of six Charpy specimens failed during the SCC tests. The main goal of this analysis was an investigation anddescription of failure mechanisms taking place during SCC of 304L stainless steel.

Czech name

—

Czech description

—

Type

D - Article in proceedings

CEP classification

JK - Corrosion and material surfaces

OECD FORD branch

—

Project

—

Continuities

Z - Vyzkumny zamer (s odkazem do CEZ)

Publication year

2009

Confidentiality

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Article name in the collection

Fractography 2009

ISBN

978-80-968543-8-7

ISSN

—

e-ISSN

—

Number of pages

8

Pages from-to

—

Publisher name

Institute of Materials Research SAS

Place of publication

Košice

Event location

Stará Lesná

Event date

Nov 8, 2009

Type of event by nationality

WRD - Celosvětová akce

UT code for WoS article

—