Fatigue behavior of filled rubber material
Original language description
The understanding of the fatigue behavior of rubber in the dependence on the complex stress loading conditions, which is the reason for crack initiations and its propagation, is a subject of high scientific and application oriented interest to understand and improve durability and life service of rubber products. In the present work, the pure rubbers; natural rubber (NR) and butadiene rubber (BR) as well as binary rubber blend NR/BR at the blend ratio 50/50 filled with varied content 10, 30 and 50 phr of carbon black (CB) with commonly encountered rubber additives were subjected to fatigue loading conditions under sinusoidal waveform up to 1.000.000 of loading cycles. The focus was to observe the fatigue behavior of each of the rubber component as well as the rubber blend. This paper describes the fatigue behavior of different rubber materials for describing the influence of strain crystallization as well as of filler content on stress evaluation during increasing number of fatigue cycles.
Czech name
—
Czech description
—

Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach

Publication year
2016
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)