The study of fatigue behavior of thermally aged rubber based on natural rubber and butadiene rubber

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F70883521%3A28610%2F17%3A63518258" target="_blank" >RIV/70883521:28610/17:63518258 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
The study of fatigue behavior of thermally aged rubber based on natural rubber and butadiene rubber
Original language description
This work is focused on investigation of the influence of thermal aging on fatigue behavior of carbon black filled rubber compounds which have been based on Natural Rubber (NR), Butadiene Rubber (BR) and their blend with ratio 50/50. The thermal aging was performed in thermal chamber at varied temperatures 30, 70 and 110°C for 720 hours. Firstly, the influence of thermal aging on mechanical behavior under quasi-static tensile test followed by Dynamic Mechanical Analysis (DMA) has been investigated. The fatigue behavior under sinusoidal waveform loading conditions has quantitatively been analyzed by using of dynamic testing equipment Tear and Fatigue Analyzer. The aim of this work was to investigate the influence of thermal aging on the fatigue behavior of rubber based on varied rubber types to understand the relationship between the thermal degradative processes occurred in rubber matrix under thermal aging and fatigue life. From the experimental work it was concluded based on all used testing methods, that the presence of BR rubber enhances the resistance against thermal aging and thus could be used as an efficient component reducing the aging degradation in rubber blend systems.
Czech name
—
Czech description
—

Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2017
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Article name in the collection
Constitutive Models for Rubber X: Proceedings of the European Conference on Constitutive Models for Rubbers X
ISBN
978-1-138-03001-5
ISSN
—
e-ISSN
neuvedeno
Number of pages
6
Pages from-to
365-370
Publisher name
CRC Press Balkema publishers
Place of publication
Leiden
Event location
Mnichov
Event date
Aug 28, 2017
Type of event by nationality
EUR - Evropská akce
UT code for WoS article
—

Similar results(10)