D. 1. Application of slow strain rate test for evaluation of resistance of duplex stainless steels to sulphide stress corrosion cracking
D: 1. Slow strain rate test was applied to evaluate resistance of duplex stainless steels SAF 2205 and SAF 2507 to sulphide stress corrosion cracking in environment of 20% NaCl-H2S with pH=4 at 80 C....
JK - Koroze a povrchové úpravy materiálu
- 2000 •
- D
Rok uplatnění
D - Stať ve sborníku
Stress Corrosion Cracking Susceptibility of Austenitic Stainless Steels in Supercritical Water Conditions
The presented paper summarizes the results of general corrosion and stress corrosion cracking susceptibility tests in supercritical water, studied for austenitic stainless steel 316L, with the aim to identify maxim...
JL - Únava materiálu a lomová mechanika
- 2011 •
- Jx •
- Link
Rok uplatnění
Jx - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
Výsledek na webu
D: 2. Application of monitoring of corrosion elongation for evaluation of resistance of duplex stainless steels to sulphide stress corrosion cracking in constant loading tests
D: 2. Monitoring of corrosion elongation in constant loading tests was applied to evaluate corrosion resistance of duplex stainless steel 2205 to sulphide stress corrosion cracking in environment of 20% Na...
JK - Koroze a povrchové úpravy materiálu
- 2001 •
- D
Rok uplatnění
D - Stať ve sborníku
Corrosion tests of high alloyed duplex steels at slow strain rate testing
The aim of the study is to verify the most important characteristics quantifying the corrosion resistivity of the steels especially in the media containing chloride ions......
JK - Koroze a povrchové úpravy materiálu
- 2006 •
- D
Rok uplatnění
D - Stať ve sborníku
Drop Evaporation Test for stress corrosion cracking study
The drop evaporation test (DET) was developed for study of stainless steels resistance to stress corrosion cracking (SCC) at elevated temperatures 120 - 300 °C under and long-time service exposition was tested unde...
JG - Hutnictví, kovové materiály
- 2003 •
- D
Rok uplatnění
D - Stať ve sborníku
Corrosion behaviour of Stainless high alloyed steels and nickel alloys in chloride media
Corrosion behaviour of Stainless high alloyed steels and nickel alloys in chloride media...
JK - Koroze a povrchové úpravy materiálu
- 2006 •
- A
Rok uplatnění
A - Audiovizuální tvorba
Stress corrosion cracking evaluation of high alloy steel (X2CrNiMoN 22-5-3) by DET
In the paper is studied the initiation and propagation of stress corrosion materials resistance to stress corrosion cracking (SCC). The initiation and propagation with sufficient resistance to a general corrosi...
JG - Hutnictví, kovové materiály
- 2004 •
- Jx
Rok uplatnění
Jx - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
Application of DET for the study of stress corrosion cracking initiation of high alloy materials
In the contribution is studied the initiation and propagation of stress corrosion cracking of high alloy materials from corrosion pits by the travelling microscope method under drop evaporation test (DET) condition...
JG - Hutnictví, kovové materiály
- 2003 •
- D
Rok uplatnění
D - Stať ve sborníku
The effects of stress on corrosion behavior of SIMP martensitic steel in static liquid lead-bismuth eutectic
testing. The stress corrosion was performed in static lead-bismuth eutectic at 300. The effect of stress on corrosion rate at different temperatures was investigated investigating the stress<...
Materials engineering
- 2021 •
- Jimp •
- Link
Rok uplatnění
Jimp - Článek v periodiku v databázi Web of Science
Výsledek na webu
Study of corrosion properties of high alloyed structural materials used in power industry
Study of corrosion properties of high alloyed structural materials used in power industry...
JK - Koroze a povrchové úpravy materiálu
- 2007 •
- D
Rok uplatnění
D - Stať ve sborníku