Determination of resistance to intergranular corrosio of stainless steels.
The methodology describes procedure of corrosion tests for the determination of resistance to intergranular corrosion of stainless steels.
JG - Hutnictví, kovové materiály
- 2015 •
- NmetC •
- Odkaz
Rok uplatnění
NmetC - Metodiky certifikované oprávněným orgánem
Výsledek na webu
Competition of Transgranular and Intergranular Failure at Brittle Fracture Initiation.
The aim of the study is to analyse micromechanical aspects of intergranular initiation of brittle fracture as a micromechanism that can be well susceptible or this work is to quantify causes and characteristics goveming the intergranular...
JL - Únava materiálu a lomová mechanika
- 2001 •
- D
Rok uplatnění
D - Stať ve sborníku
Physical metallurgy of intergranular failures in martensite
Physical metallurgy of intergranular failures in martensite...
JG - Hutnictví, kovové materiály
- 1999 •
- D
Rok uplatnění
D - Stať ve sborníku
Anomalies associated with intergranular currents in a Bi-2223 monocore tape.
Characterization of the anomaly associated with intergranular currents. Average magnetic moments, in broad temperature range shows that the anomaly extends up to irreversibility field....
BM - Fyzika pevných látek a magnetismus
- 2001 •
- D
Rok uplatnění
D - Stať ve sborníku
Intergranular sensibility of alloy 800
Cyclic polarisation measurements (EPR-test) make it possible to derive the alloys susceptibility tu intergranular pitting and cravice corrosion from characteristic potentials and other quantities determined in the EPR-test....
JK - Koroze a povrchové úpravy materiálu
- 2005 •
- D
Rok uplatnění
D - Stať ve sborníku
Micromechanical aspects of transgranular and intergranular failure competition
that control the intergranular fracture initiation and occurrence of this fracture cooling treatment was applied in order to induce intergranular embrittlement for intergranular failure has been followed showing capability...
JL - Únava materiálu a lomová mechanika
- 2006 •
- D
Rok uplatnění
D - Stať ve sborníku
Micromechanical aspects of transgranular and intergranular failure competition
that control the intergranular fracture initiation and occurrence of this fracture cooling treatment was applied in order to induce intergranular embrittlement for intergranular failure has been followed showing capability...
JL - Únava materiálu a lomová mechanika
- 2006 •
- D
Rok uplatnění
D - Stať ve sborníku
Transgranular and intergranular failure competition as a manifestation of steel degradation
that control the intergranular fracture initiation and occurrence of this fracture cooling treatment was applied in order to induce intergranular embrittlement for intergranular failure has been followed showing capability...
JL - Únava materiálu a lomová mechanika
- 2006 •
- D
Rok uplatnění
D - Stať ve sborníku
INTERGRANULAR AND PITTING CORROSION RESISTANCE OF SUPERMARTENSITIC STEEL OF 13Cr6Ni2,5Mo TYPE
Pitting and intergranular corrosion resistance of supermartenzitic steel 13Cr6Ni2,5MoTi and its weld joints was evaluated by potentiodynamic and electrochemical and intergranular attack of this type of steel. Weld joints did not sho...
JG - Hutnictví, kovové materiály
- 2010 •
- Jx
Rok uplatnění
Jx - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
Operational degradation and competition of cleavage and intergranular failure.
Original scientific paper dealing with Operational degradation and competition of cleavage and intergranular failure.
JL - Únava materiálu a lomová mechanika
- 2000 •
- D
Rok uplatnění
D - Stať ve sborníku