Depth profiling of W–Ta based fusion-relevant samples using picosecond laser ablation

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216224%3A14310%2F24%3A00135957" target="_blank" >RIV/00216224:14310/24:00135957 - isvavai.cz</a>
Result on the web
<a href="https://www.sciencedirect.com/science/article/pii/S0584854724000740" target="_blank" >https://www.sciencedirect.com/science/article/pii/S0584854724000740</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.sab.2024.106930" target="_blank" >10.1016/j.sab.2024.106930</a>

Result language
angličtina
Original language name
Depth profiling of W–Ta based fusion-relevant samples using picosecond laser ablation
Original language description
This study presents a detailed picosecond LIBS analysis of WTa coatings on Molybdenum substrate with varying layer thicknesses for fusion relevant applications. Ps-LIBS is performed on three WTa layers; two without deuterium (∼7 μm thickness) and one with deuterium (∼1 μm thickness). The LIBS measurements are conducted under argon gas flow at 5±0.2 mbar pressure with different laser pulse energies (1 mJ, 3 mJ) and 100 spectra are recorded consecutively at one spot on the sample for different set of gate delay/gate width (200/200 ns, 300/300 ns, 450/450 ns). The obtained LIBS and Glow-Discharge Optical Emission Spectroscopy (GDOES) depth profiles are compared with the confocal microscopic measurements showing good agreement. Additionally, the ablation rate and layer thickness are calculated for different experimental conditions. The Calibration-Free LIBS approach is used for elemental analysis and the results are compared with GDOES results. The capability of ps-LIBS to quantify Ta in WTa alloy is explored for 2 at.% of Ta. However, due to higher ablation rate of laser and thin coating in WTaD sample, the layer is irradiated in few laser pulse and therefore, CF-LIBS analysis is not performed for it.
Czech name
—
Czech description
—

Type
J<sub>imp</sub> - Article in a specialist periodical, which is included in the Web of Science database
CEP classification
—
OECD FORD branch
10305 - Fluids and plasma physics (including surface physics)

Project
<a href="/en/project/LM2018097" target="_blank" >LM2018097: R&D centre for plasma and nanotechnology surface modifications</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Publication year
2024
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)