Identification of surface active components in glass forming melts by thermodynamic model

Result code in IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216275%3A25310%2F21%3A39918007" target="_blank" >RIV/00216275:25310/21:39918007 - isvavai.cz</a>

Result on the web

<a href="https://www.sciencedirect.com/science/article/pii/S0022309320305275?via%3Dihub" target="_blank" >https://www.sciencedirect.com/science/article/pii/S0022309320305275?via%3Dihub</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.jnoncrysol.2020.120415" target="_blank" >10.1016/j.jnoncrysol.2020.120415</a>

Result language

angličtina

Original language name

Identification of surface active components in glass forming melts by thermodynamic model

Original language description

Nine compositional series of 15(Na2O, K2O).10(CaO, ZnO).75(ZrO2, SiO2) glass-forming melts were studied, all with the ZrO2 content of 0, 1, 3, 5 and 7 mol.%. The investigated glass compositions were obtained by equimolar substitutions ZrO2 / SiO2, ZnO / CaO and K2O / Na2O. Surface tension of studied glassforming melts was determined by the sessile and pendant drop profile numerical analysis in the temperature range (1250 1500) °C. The experimental values of melt density were used. The linear temperature dependence of surface tension was observed for all samples with only small differences between values obtained from sessile and pendant drop profiles. The Shakhmatkin and Vedishcheva thermodynamic model (TDM) was evaluated for each glass melt at temperature of 1400 degrees C. The total number of 36 components was considered in TDM. Only 26 components were present with non-negligible equilibrium amount. The surface tension was described by the multilinear function of equilibrium amounts of statistically independent non-negligible components of the TDM. The surface active components were identified by negative values of their coefficients. Such way the N3S8 and C2ZrS4 were identified as &quot;strongly&quot; surface active and NCS5 and KS4 as probably surface active. Regarding the oxide compositional point of view, the surface tension was mostly influenced by ZnO (increase with the addition of the oxide) and by K2O (decrease with the addition of the oxide).

Czech name

—

Czech description

—

Type

J_imp - Article in a specialist periodical, which is included in the Web of Science database

CEP classification

—

OECD FORD branch

20501 - Materials engineering

Project

—

Continuities

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Publication year

2021

Confidentiality

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Name of the periodical

Journal of Non-Crystalline Solids

ISSN

0022-3093

e-ISSN

—

Volume of the periodical

551

Issue of the periodical within the volume

January

Country of publishing house

NL - THE KINGDOM OF THE NETHERLANDS

Number of pages

7

Pages from-to

"120415-1"-"120415-7"

UT code for WoS article

000589928500005

EID of the result in the Scopus database

2-s2.0-85091978292