Stress-Controlled Fatigue Testing of E-Glass Epoxy Composite: Monitoring of Micro-Damage

Result code in IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F49777513%3A23520%2F15%3A43925136" target="_blank" >RIV/49777513:23520/15:43925136 - isvavai.cz</a>

Result on the web

<a href="http://dx.doi.org/10.4028/www.scientific.net/AMM.732.143" target="_blank" >http://dx.doi.org/10.4028/www.scientific.net/AMM.732.143</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.4028/www.scientific.net/AMM.732.143" target="_blank" >10.4028/www.scientific.net/AMM.732.143</a>

Result language

angličtina

Original language name

Stress-Controlled Fatigue Testing of E-Glass Epoxy Composite: Monitoring of Micro-Damage

Original language description

The paper deals with progressive and fatigue damage of a long fiber E-glass epoxy composite, its residual stiffness degradation and corresponding transverse matrix crack density induced by load-controlled tension. The crack density increases with increasing number of cycles or load. Consequently, residual stiffness of the laminate decreases. It has been concluded that progressive/fatigue damage of the laminate is not a continuous homogenous process but the series of discrete sudden events emerging at ply level. The paper deals with progressive and fatigue damage of a long fiber E-glass epoxy composite, its residual stiffness degradation and corresponding transverse matrix crack density induced by load-controlled tension. The crack density increases with increasing number of cycles or load. Consequently, residual stiffness of the laminate decreases. It has been concluded that progressive/fatigue damage of the laminate is not a continuous homogenous process but the series of discrete sud

Czech name

—

Czech description

—

Type

J_x - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)

CEP classification

JI - Composite materials

OECD FORD branch

—

Project

Result was created during the realization of more than one project. More information in the Projects tab.

Continuities

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year

2015

Confidentiality

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Name of the periodical

Applied Mechanics and Materials

ISSN

1660-9336

e-ISSN

—

Volume of the periodical

732

Issue of the periodical within the volume

neuveden

Country of publishing house

CH - SWITZERLAND

Number of pages

4

Pages from-to

143-146

UT code for WoS article

—

EID of the result in the Scopus database

—