Properties of polyimide, polyetheretherketone and polyethyleneterephthalate implanted by Ni ions to high fluences
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22310%2F12%3A43894285" target="_blank" >RIV/60461373:22310/12:43894285 - isvavai.cz</a>
Alternative codes found
RIV/61389005:_____/12:00370863 RIV/61389013:_____/12:00370863 RIV/44555601:13440/12:43883914
Result on the web
<a href="http://dx.doi.org/10.1016/j.nimb.2011.01.109" target="_blank" >http://dx.doi.org/10.1016/j.nimb.2011.01.109</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.nimb.2011.01.109" target="_blank" >10.1016/j.nimb.2011.01.109</a>
Alternative languages
Result language
angličtina
Original language name
Properties of polyimide, polyetheretherketone and polyethyleneterephthalate implanted by Ni ions to high fluences
Original language description
Polyimide (PI), polyetheretherketone (PEEK) and polyethyleneterephthalate (PET) were implanted with 40 keV Ni+ ions at RT to the fluences (0.25-1.5) x 10(17) cm(-2) at ion current density of 4 mu A cm(-2). Then some of the samples were annealed at the temperatures close to the polymer glassy transition temperature. Depth profiles of the Ni atoms in the as implanted and annealed samples were determined by RBS method. The profiles in the as implanted samples agree reasonably with those simulated using TRYDIN code. The implanted Ni atoms tend to aggregate into nano-particles, the size and distribution of which was determined from TEM images. The nano-particle size increases with increasing ion fluence. Subsequent annealing leads to a reduction in the nanoparticle size. The surface morphology of the implanted and annealed samples was studied using AFM. The changes in the polymer sheet resistance of the implanted and annealed samples were measured by standard two-point technique. The sheet
Czech name
—
Czech description
—
Classification
Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JJ - Other materials
OECD FORD branch
—
Result continuities
Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Others
Publication year
2012
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Name of the periodical
Nuclear Instruments and Methods in Physics Research, Section B
ISSN
0168-583X
e-ISSN
—
Volume of the periodical
272
Issue of the periodical within the volume
20120201
Country of publishing house
NL - THE KINGDOM OF THE NETHERLANDS
Number of pages
4
Pages from-to
396-399
UT code for WoS article
000301159900091
EID of the result in the Scopus database
—