Grain refining of Cu and Ni-Ti shape memory alloys by ECAP process
Original language description
This paper was aimed at verification of functionally of the ECAP technology at extrusion of the copper and Ni-TI alloys. Cross-section of original samples was 8x8mm and thein length was 32mm. The samples of Cu were extruded at room temperature. For the samples of Ni-Ti alloys was used the two-stage pressing, when the samples were at temperature of approx. T1=520ºC and T2= 420ºC. In order to increase the concentration of deformation in volume of the samples, the samples were turned around theinlongitudinal axis by 90º after individual passes and they were extruded again.
Czech name
Zjemňění zrna Cu a Ni-Ti tvarově paměťových slitin zpracované ECAP
Czech description
Tento článek se věnoval ověření funkčnosri ECAP technologie na protlačování mědi a Ni-Ti slitin. Průřez původních vzorků bzl 8x8mm a jejich délka byla 32mm. Vzorky mědi byly protlačovány při pokojové teplotě.Pro vzorky Ni-Ti slitin bylo použito dvoustupňového protlačování, kdy vzorky byly při teplotě asi T1=520ºC a T2=420ºC. Podle zvyšující se koncentrace deformace v celém vzorku, vzorky byly po individuálních průchodech pootočeny kolem osy o 90º a znovu protlačeny .