Synergy of precipitation, deformation and transformation hardening in steels with higher copper content
Anotace anglicky
Structural steels with higher copper content have bee a subject to material research in the last two decades. The main advantage of the concept of steels with controlled copper content is final very good mechanical properties after thermal or thermo-mechanical treatment. They are achieved due to a very favorable effect of precipitation hardening, which also reduces material ductility relatively a little. The proposed project will investigate simultaneous effect of different reinforcement mechanisms for several variants of structural low-alloyed steels with higher copper content. It will be all about synergy of transformation, deformation and precipitation hardening, moreover it will be also tried to use solid solution hardening and hardening due to grain refinement. The effect of the influence of copper in the amount of up to 1.5% will be amplified, B and Ti will be alternatively added to experimental melts. The elements in combination with copper slow decay kinetics of austenite solid solution and shift it to longer times, lower temp., and soften austenitic grain.

Kategorie VaV
ZV - Základní výzkum
CEP - hlavní obor
JG - Hutnictví, kovové materiály
CEP - vedlejší obor
—
CEP - další vedlejší obor
—
OECD FORD - odpovídající obory <br>(dle <a href="http://www.vyzkum.cz/storage/att/E6EF7938F0E854BAE520AC119FB22E8D/Prevodnik_oboru_Frascati.pdf">převodníku</a>)
20501 - Materials engineering

Důvěrnost údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Systémové označení dodávky dat
CEP21-GA0-GA-R/11:1
Datum dodání záznamu
22. 2. 2021

Podobné projekty(10)