High-temperature stability of materials based on LC3 binders

Název projektu anglicky
High-temperature stability of materials based on LC3 binders
Anotace anglicky
Limestone calcined clay cement (LC3) is a novel type of building material that provides a significant reduction of CO2 emissions by replacing of Portland cement with supplementary cementitious materials with lower CO2 footprint. Recent research has primarily focused on the production process of LC3, the mineralogical and chemical composition, and the impact on the hydration process and mechanical properties. Since the crucial aspect of the application of any material is its durability, the main goal of the project is to investigate the influence of elevated temperatures on the performance of this type of cement which has been poorly studied so far. The project will provide a complex characterization of the microstructure and mechanical, fracture, thermal, and hygric properties of LC3 materials during and after the exposure to temperatures ranging from 200 to 1200 °C. Different cooling regimes will also be performed after high temperature exposure and their effect on the residual mechanical properties and microstructure will be analysed.

Kategorie VaV
ZV - Základní výzkum
OECD FORD - hlavní obor
20101 - Civil engineering
OECD FORD - vedlejší obor
20501 - Materials engineering
OECD FORD - další vedlejší obor
—
CEP - odpovídající obory <br>(dle <a href="http://www.vyzkum.cz/storage/att/E6EF7938F0E854BAE520AC119FB22E8D/Prevodnik_oboru_Frascati.pdf">převodníku</a>)
JG - Hutnictví, kovové materiály<br>JN - Stavebnictví<br>JP - Průmyslové procesy a zpracování

Důvěrnost údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Systémové označení dodávky dat
CEP26-GA0-GA-R
Datum dodání záznamu
4. 5. 2026

Podobné projekty(10)