N-Allyl-N-methylpiperidinium bis(trifluoromethanesulfonyl)imide-A film forming ionic liquid for graphite anode of Li-ion batteries
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11310%2F12%3A10127699" target="_blank" >RIV/00216208:11310/12:10127699 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/61388980:_____/12:00387933
Výsledek na webu
<a href="http://dx.doi.org/10.1016/j.electacta.2012.03.088" target="_blank" >http://dx.doi.org/10.1016/j.electacta.2012.03.088</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.electacta.2012.03.088" target="_blank" >10.1016/j.electacta.2012.03.088</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
N-Allyl-N-methylpiperidinium bis(trifluoromethanesulfonyl)imide-A film forming ionic liquid for graphite anode of Li-ion batteries
Popis výsledku v původním jazyce
An ionic liquid. N-allyl-N-methylpiperidinium bis(trifluoromethanesulfonyl)imide PP13 center dot TFSI has been successfully tested as a solid electrolyte interface (SEI) forming agent for graphite composite anode at elevated temperature of 55 degrees C in a purely ionic liquid-based electrolyte: 0.5 m LiTFSI in a mixture of PP13 center dot TFSI-PP13TFSI (20-80 wt.%) The reversible discharge capacity was 340-350 mAh g(-1) with only a small irreversible capacity loss per cycle. The electrochemical polymerisation of the allylic double bond participates on the SEI formation on the graphite surface. In the absence of unsaturated ionic liquid, the piperidinium cation is co-intercalated into graphite and causes its exfoliation with permanent loss of capacity.The electrolyte is thermally stable up to 320 degrees C and reasonably conductive (2.4 mS cm(-1) at 55 degrees C).
Název v anglickém jazyce
N-Allyl-N-methylpiperidinium bis(trifluoromethanesulfonyl)imide-A film forming ionic liquid for graphite anode of Li-ion batteries
Popis výsledku anglicky
An ionic liquid. N-allyl-N-methylpiperidinium bis(trifluoromethanesulfonyl)imide PP13 center dot TFSI has been successfully tested as a solid electrolyte interface (SEI) forming agent for graphite composite anode at elevated temperature of 55 degrees C in a purely ionic liquid-based electrolyte: 0.5 m LiTFSI in a mixture of PP13 center dot TFSI-PP13TFSI (20-80 wt.%) The reversible discharge capacity was 340-350 mAh g(-1) with only a small irreversible capacity loss per cycle. The electrochemical polymerisation of the allylic double bond participates on the SEI formation on the graphite surface. In the absence of unsaturated ionic liquid, the piperidinium cation is co-intercalated into graphite and causes its exfoliation with permanent loss of capacity.The electrolyte is thermally stable up to 320 degrees C and reasonably conductive (2.4 mS cm(-1) at 55 degrees C).
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CG - Elektrochemie
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2012
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Electrochimica Acta
ISSN
0013-4686
e-ISSN
—
Svazek periodika
71
Číslo periodika v rámci svazku
June
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
5
Strana od-do
22-26
Kód UT WoS článku
000304510900004
EID výsledku v databázi Scopus
—