Correlation of crystal structure and magnetic properties of Co((1-x))NixFe2O4/SiO2 nanocomposites

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11310%2F13%3A10159111" target="_blank" >RIV/00216208:11310/13:10159111 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68378271:_____/13:00394535 RIV/61388980:_____/13:00394535

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.jmmm.2013.01.005" target="_blank" >http://dx.doi.org/10.1016/j.jmmm.2013.01.005</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.jmmm.2013.01.005" target="_blank" >10.1016/j.jmmm.2013.01.005</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Correlation of crystal structure and magnetic properties of Co((1-x))NixFe2O4/SiO2 nanocomposites

Popis výsledku v původním jazyce

The Co((1-x))NixFe2O4/SiO2 (x=0.0, 0.2, 0.4, 0.6, 0.8, 1.0) nanocomposites were prepared using the sol-gel method and characterized by Powder X-ray Diffraction (PXRD), Energy Dispersive X-ray Spectroscopy (EDX) and magnetic measurements. Moreover, Mossbauer spectroscopy (performed at room temperature and at 4.2 K with applied field 6 T) was performed to determine the cation distribution within the spinel network. The PXRD measurements confirmed the presence of the spinel phase in all samples. The particle diameters, obtained from the PXRD, were found out to vary between 15 and 24 nm. The lattice parameters decrease linearly with increasing content of the Ni2+ ions. The ZFC (zero field cooled) and FC (field cooled) measurements of the magnetization showed that the blocking temperature is well above the room temperature for all samples. Both the coercivity and the saturation magnetization decrease linearly with increasing content of the Ni2+ ions. The room temperature Mossbauer spectra e

Název v anglickém jazyce

Correlation of crystal structure and magnetic properties of Co((1-x))NixFe2O4/SiO2 nanocomposites

Popis výsledku anglicky

The Co((1-x))NixFe2O4/SiO2 (x=0.0, 0.2, 0.4, 0.6, 0.8, 1.0) nanocomposites were prepared using the sol-gel method and characterized by Powder X-ray Diffraction (PXRD), Energy Dispersive X-ray Spectroscopy (EDX) and magnetic measurements. Moreover, Mossbauer spectroscopy (performed at room temperature and at 4.2 K with applied field 6 T) was performed to determine the cation distribution within the spinel network. The PXRD measurements confirmed the presence of the spinel phase in all samples. The particle diameters, obtained from the PXRD, were found out to vary between 15 and 24 nm. The lattice parameters decrease linearly with increasing content of the Ni2+ ions. The ZFC (zero field cooled) and FC (field cooled) measurements of the magnetization showed that the blocking temperature is well above the room temperature for all samples. Both the coercivity and the saturation magnetization decrease linearly with increasing content of the Ni2+ ions. The room temperature Mossbauer spectra e

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)<br>I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2013

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Magnetism and Magnetic Materials

ISSN

0304-8853

e-ISSN

—

Svazek periodika

334

Číslo periodika v rámci svazku

may

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

5

Strana od-do

102-106

Kód UT WoS článku

000315744100017

EID výsledku v databázi Scopus

—