Single crystals of guanidinium zinc sulfate, [C(NH2)(3)](2)Zn(SO4)(2) - growth, structure, vibrational spectroscopy and stimulated Raman scattering
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11310%2F15%3A10313141" target="_blank" >RIV/00216208:11310/15:10313141 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1515/zkri-2015-1839" target="_blank" >http://dx.doi.org/10.1515/zkri-2015-1839</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1515/zkri-2015-1839" target="_blank" >10.1515/zkri-2015-1839</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Single crystals of guanidinium zinc sulfate, [C(NH2)(3)](2)Zn(SO4)(2) - growth, structure, vibrational spectroscopy and stimulated Raman scattering
Popis výsledku v původním jazyce
Large single crystals of the tetragonal (space group I (4) over bar 2d) guanidinium zinc sulfate, [C(NH2)(3)](2)Zn(SO4)(2), were grown and the crystal structure was redetermined. Vibrational spectra obtained by Raman and IR investigations are presented,together with an assignment of the observed vibration modes. Precise refractive index data in the wavelength range from 0.365 to 1.083 mu m are given. [C(NH2)(3)](2)Zn(SO4)(2) is introduced as a new stimulated Raman scattering (SRS)-active crystal with three SRS-active vibration modes with omega(SRS1) approximate to 985 cm(-1), omega(SRS2) approximate to 3390 cm(-1) and omega(SRS3) approximate to 1015 cm(-1). They allow for the generation of broadband nonlinear emission via chi(3)-(SRS and Raman-inducedfour wave mixing, RFWM) as well as cascaded chi(2)<->chi(3)-processes.
Název v anglickém jazyce
Single crystals of guanidinium zinc sulfate, [C(NH2)(3)](2)Zn(SO4)(2) - growth, structure, vibrational spectroscopy and stimulated Raman scattering
Popis výsledku anglicky
Large single crystals of the tetragonal (space group I (4) over bar 2d) guanidinium zinc sulfate, [C(NH2)(3)](2)Zn(SO4)(2), were grown and the crystal structure was redetermined. Vibrational spectra obtained by Raman and IR investigations are presented,together with an assignment of the observed vibration modes. Precise refractive index data in the wavelength range from 0.365 to 1.083 mu m are given. [C(NH2)(3)](2)Zn(SO4)(2) is introduced as a new stimulated Raman scattering (SRS)-active crystal with three SRS-active vibration modes with omega(SRS1) approximate to 985 cm(-1), omega(SRS2) approximate to 3390 cm(-1) and omega(SRS3) approximate to 1015 cm(-1). They allow for the generation of broadband nonlinear emission via chi(3)-(SRS and Raman-inducedfour wave mixing, RFWM) as well as cascaded chi(2)<->chi(3)-processes.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CA - Anorganická chemie
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA14-05506S" target="_blank" >GA14-05506S: Krystalové inženýrství nových molekulárních krystalů pro nelineární optiku</a><br>
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Zeitschrift für Kristallographie - Crystalline Materials
ISSN
2194-4946
e-ISSN
—
Svazek periodika
230
Číslo periodika v rámci svazku
11
Stát vydavatele periodika
DE - Spolková republika Německo
Počet stran výsledku
11
Strana od-do
639-649
Kód UT WoS článku
000364317300003
EID výsledku v databázi Scopus
2-s2.0-84946882152