Subgap photoluminescence spectroscopy of nanocrystalline diamond films

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F09%3A00206305" target="_blank" >RIV/00216208:11320/09:00206305 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68378271:_____/09:00337120

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Subgap photoluminescence spectroscopy of nanocrystalline diamond films

Popis výsledku v původním jazyce

We report on the effect of ambient conditions and UV irradiation on the subgap photoluminescence of nanocrystalline diamond prepared by microwave plasma enhanced chemical vapour deposition. We measured the photoluminescence of self-supporting membranes of thickness about 290 nm with the grain size up to 40 nm under variable ambient conditions - pressure, temperature, air, nitrogen and helium atmospheres. We have found that intensity of photoluminescence of samples kept under low pressure increases during the time. The photoluminescence intensity of samples under low pressure depends on sample temperature with maximum at about 260 K. The photoluminescence increase can be enhanced substantially by UV irradiation (325 nm) of the sample under certain conditions: temperature greater than 280 K, low pressure of ambient atmosphere. We interpret the experimental results in terms of desorption of water molecules and their interaction with the of individual diamond nanocrystals in the membrane.

Název v anglickém jazyce

Subgap photoluminescence spectroscopy of nanocrystalline diamond films

Popis výsledku anglicky

We report on the effect of ambient conditions and UV irradiation on the subgap photoluminescence of nanocrystalline diamond prepared by microwave plasma enhanced chemical vapour deposition. We measured the photoluminescence of self-supporting membranes of thickness about 290 nm with the grain size up to 40 nm under variable ambient conditions - pressure, temperature, air, nitrogen and helium atmospheres. We have found that intensity of photoluminescence of samples kept under low pressure increases during the time. The photoluminescence intensity of samples under low pressure depends on sample temperature with maximum at about 260 K. The photoluminescence increase can be enhanced substantially by UV irradiation (325 nm) of the sample under certain conditions: temperature greater than 280 K, low pressure of ambient atmosphere. We interpret the experimental results in terms of desorption of water molecules and their interaction with the of individual diamond nanocrystals in the membrane.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BH - Optika, masery a lasery

OECD FORD obor

—

Projekt

<a href="/cs/project/KAN400100701" target="_blank" >KAN400100701: Funkční hybridní nanosystémy polovodičů a kovů s organickými látkami (FUNS)</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Diamond and Related Materials

ISSN

0925-9635

e-ISSN

—

Svazek periodika

18

Číslo periodika v rámci svazku

5-8

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

3

Strana od-do

—

Kód UT WoS článku

000267737000019

EID výsledku v databázi Scopus

—