The optimization of ECAP conditions to achieve high strain-rate superplasticity in a Zr- and Sc-modified AA 7075 aluminum alloy

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F09%3A00206970" target="_blank" >RIV/00216208:11320/09:00206970 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

The optimization of ECAP conditions to achieve high strain-rate superplasticity in a Zr- and Sc-modified AA 7075 aluminum alloy

Popis výsledku v původním jazyce

An AA 7075 aluminum alloy with Zr and Sc additions was subjected to 6-8 ECAP passes at 120, 170, and 220 °C in order to examine the effect of the pressing conditions on the microstructural characteristics and the consequences for high-temperature mechanical properties. Using the method of EBSD, a decrease in pressing temperature was found to lead to a more pronounced refinement of the microstructure and a higher fraction of high-angle grain boundaries, but at the same time compromised the ability of theAl3 (Zr, Sc) phase to stabilize the ultra-fine-grained microstructure at elevated temperatures. Optimum superplastic properties were therefore achieved after pressing at the intermediate temperature of 170 °C. The material exhibited high strain-rate superplasticity with a ductility of 650 % at an initial strain rate of 1 x 10-1 s-1.

Název v anglickém jazyce

The optimization of ECAP conditions to achieve high strain-rate superplasticity in a Zr- and Sc-modified AA 7075 aluminum alloy

Popis výsledku anglicky

An AA 7075 aluminum alloy with Zr and Sc additions was subjected to 6-8 ECAP passes at 120, 170, and 220 °C in order to examine the effect of the pressing conditions on the microstructural characteristics and the consequences for high-temperature mechanical properties. Using the method of EBSD, a decrease in pressing temperature was found to lead to a more pronounced refinement of the microstructure and a higher fraction of high-angle grain boundaries, but at the same time compromised the ability of theAl3 (Zr, Sc) phase to stabilize the ultra-fine-grained microstructure at elevated temperatures. Optimum superplastic properties were therefore achieved after pressing at the intermediate temperature of 170 °C. The material exhibited high strain-rate superplasticity with a ductility of 650 % at an initial strain rate of 1 x 10-1 s-1.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F07%2F0303" target="_blank" >GA106/07/0303: Úloha hranic zrn při vysokoteplotní plastické deformaci jemnozrnných materiálů</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

International Journal of Materials Research

ISSN

1862-5282

e-ISSN

—

Svazek periodika

100

Číslo periodika v rámci svazku

6

Stát vydavatele periodika

DE - Spolková republika Německo

Počet stran výsledku

7

Strana od-do

—

Kód UT WoS článku

000267933300024

EID výsledku v databázi Scopus

—