Recovery and recrystallization behavior of aluminum processed by extrusion-preceded equal channel angular pressing

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F09%3A00207037" target="_blank" >RIV/00216208:11320/09:00207037 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—

Jazyk výsledku
angličtina
Název v původním jazyce
Recovery and recrystallization behavior of aluminum processed by extrusion-preceded equal channel angular pressing
Popis výsledku v původním jazyce
High-purity aluminum was severely plastically deformed by miniaturized extrusion-preceded ECAP as well as by cold rolling. Isochronal and isothermal annealing was performed to investigate the recovery and recrystallization behavior by measuring the development of Vickers microhardness and electrical resistivity. Both processes were found to take place which was verified by TEM and EBSD observations.
Název v anglickém jazyce
Recovery and recrystallization behavior of aluminum processed by extrusion-preceded equal channel angular pressing
Popis výsledku anglicky
High-purity aluminum was severely plastically deformed by miniaturized extrusion-preceded ECAP as well as by cold rolling. Isochronal and isothermal annealing was performed to investigate the recovery and recrystallization behavior by measuring the development of Vickers microhardness and electrical resistivity. Both processes were found to take place which was verified by TEM and EBSD observations.

Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—

Rok uplatnění
2009
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Popis výsledku