Strain Release From Pre-Deformed Ni53.6Mn27.1Ga19.3 Shape Memory Alloy During Thermal Cycling

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F09%3A00207227" target="_blank" >RIV/00216208:11320/09:00207227 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Strain Release From Pre-Deformed Ni53.6Mn27.1Ga19.3 Shape Memory Alloy During Thermal Cycling

Popis výsledku v původním jazyce

A polycrystalline Ni53.6Mn27.1Ga19.3 shape memory alloy was deformed in compression in four steps up to final deformation of 3.8 % at room temperature. After each deformation step relative elongation was measured in two thermal cycles in the temperaturerange of 300 K to 640 K, where thermoelastic martensitic phase transformation occurs. The one-way shape memory effect, the two-way shape memory effect and dislocation recovery were observed after deformation of the alloy and their relation to other mechanical characteristics of the alloy was discussed. 60 % of total strain was recovered after two thermal cycles after the last deformation step.

Název v anglickém jazyce

Strain Release From Pre-Deformed Ni53.6Mn27.1Ga19.3 Shape Memory Alloy During Thermal Cycling

Popis výsledku anglicky

A polycrystalline Ni53.6Mn27.1Ga19.3 shape memory alloy was deformed in compression in four steps up to final deformation of 3.8 % at room temperature. After each deformation step relative elongation was measured in two thermal cycles in the temperaturerange of 300 K to 640 K, where thermoelastic martensitic phase transformation occurs. The one-way shape memory effect, the two-way shape memory effect and dislocation recovery were observed after deformation of the alloy and their relation to other mechanical characteristics of the alloy was discussed. 60 % of total strain was recovered after two thermal cycles after the last deformation step.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

International Journal of Materials Research

ISSN

1862-5282

e-ISSN

—

Svazek periodika

100

Číslo periodika v rámci svazku

6

Stát vydavatele periodika

DE - Spolková republika Německo

Počet stran výsledku

3

Strana od-do

—

Kód UT WoS článku

000267933300035

EID výsledku v databázi Scopus

—