Structural characterization of H plasma-doped ZnO single crystals by positron annihilation spectroscopies

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F10%3A10064255" target="_blank" >RIV/00216208:11320/10:10064255 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Structural characterization of H plasma-doped ZnO single crystals by positron annihilation spectroscopies

Popis výsledku v původním jazyce

Nominally undoped, hydrothermally grown ZnO single crystals have been investigated before and after exposure to remote H plasma. Structural characterizations have been made by various positron annihilation spectroscopies (continuous and pulsed slow positron beams, conventional lifetime). The content of bound hydrogen (H-b) before and after the remote H plasma treatment at the polished side of the crystals was determined at depths of 100 and 600 nm, respectively, using nuclear reaction analysis. At a depth of 100 nm, H-b increased from (11.8+-2.5) to (48.7+-7.6)x10^19 cm^-3 after remote H plasma treatment, whereas at 600 nm no change in H-b was observed.

Název v anglickém jazyce

Structural characterization of H plasma-doped ZnO single crystals by positron annihilation spectroscopies

Popis výsledku anglicky

Nominally undoped, hydrothermally grown ZnO single crystals have been investigated before and after exposure to remote H plasma. Structural characterizations have been made by various positron annihilation spectroscopies (continuous and pulsed slow positron beams, conventional lifetime). The content of bound hydrogen (H-b) before and after the remote H plasma treatment at the polished side of the crystals was determined at depths of 100 and 600 nm, respectively, using nuclear reaction analysis. At a depth of 100 nm, H-b increased from (11.8+-2.5) to (48.7+-7.6)x10^19 cm^-3 after remote H plasma treatment, whereas at 600 nm no change in H-b was observed.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Physica Status Solidi (A) Applications and Materials

ISSN

1862-6300

e-ISSN

—

Svazek periodika

207

Číslo periodika v rámci svazku

11

Stát vydavatele periodika

DE - Spolková republika Německo

Počet stran výsledku

11

Strana od-do

—

Kód UT WoS článku

000284055700001

EID výsledku v databázi Scopus

—