Mechanical properties and strain hardening behaviour of magnesium alloys and composites

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F10%3A10082211" target="_blank" >RIV/00216208:11320/10:10082211 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Mechanical properties and strain hardening behaviour of magnesium alloys and composites

Popis výsledku v původním jazyce

Selected magnesium alloys and composites were deformed at temperatures between room temperature and 300 °C at a constant strain rate. The testing temperature influences significantly the deformation behaviour of the materials. The flow stress decreases with increasing temperature. The work hardening rate decreases with increasing stress (strain) and temperature. Above 200 °C, a dynamic balance between hardening and softening is observed. Stress relaxation tests were performed to identify thermally activated dislocation motion. The main thermally activated process is very probably the glide of dislocations in non basal planes. The internal component of the applied stress decreases significantly with increasing temperature.

Název v anglickém jazyce

Mechanical properties and strain hardening behaviour of magnesium alloys and composites

Popis výsledku anglicky

Selected magnesium alloys and composites were deformed at temperatures between room temperature and 300 °C at a constant strain rate. The testing temperature influences significantly the deformation behaviour of the materials. The flow stress decreases with increasing temperature. The work hardening rate decreases with increasing stress (strain) and temperature. Above 200 °C, a dynamic balance between hardening and softening is observed. Stress relaxation tests were performed to identify thermally activated dislocation motion. The main thermally activated process is very probably the glide of dislocations in non basal planes. The internal component of the applied stress decreases significantly with increasing temperature.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Communications

ISSN

0341-2059

e-ISSN

—

Svazek periodika

12

Číslo periodika v rámci svazku

4

Stát vydavatele periodika

DE - Spolková republika Německo

Počet stran výsledku

8

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—