Hot Rolling of Brittle Alloy Fe-40at.%Al

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F10%3A10083333" target="_blank" >RIV/00216208:11320/10:10083333 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/46747885:24210/10:#0001600

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Hot Rolling of Brittle Alloy Fe-40at.%Al

Popis výsledku v původním jazyce

Using special protective capsules, laboratory castings made of the binary alloy of the type Fe-40at.%Al, which is difficult to form, were successfully hot rolled. The rolling was performed from thickness 20 to 13 mm with 6 or 4 passes. Regardless of theway of production and processing of the samples, rolled products without surface fracka had always been obtained, but with some pores and/or cavities and indications of internal intercrystalline cracks. It may be considered as success, with regard to thefact that initial grains were extremely coarsened due to the previous homogenization annealing 1200°C/24 hours. Structural analyses were particularly complicated by considerable heterogeneity and coarseness of the material in all phases of its processing.

Název v anglickém jazyce

Hot Rolling of Brittle Alloy Fe-40at.%Al

Popis výsledku anglicky

Using special protective capsules, laboratory castings made of the binary alloy of the type Fe-40at.%Al, which is difficult to form, were successfully hot rolled. The rolling was performed from thickness 20 to 13 mm with 6 or 4 passes. Regardless of theway of production and processing of the samples, rolled products without surface fracka had always been obtained, but with some pores and/or cavities and indications of internal intercrystalline cracks. It may be considered as success, with regard to thefact that initial grains were extremely coarsened due to the previous homogenization annealing 1200°C/24 hours. Structural analyses were particularly complicated by considerable heterogeneity and coarseness of the material in all phases of its processing.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

<a href="/cs/project/GAP107%2F10%2F0438" target="_blank" >GAP107/10/0438: Fyzikální a metalurgické aspekty deformačního chování aluminidů železa s extrémně nízkou plasticitou</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Hutnické listy

ISSN

0018-8069

e-ISSN

—

Svazek periodika

63

Číslo periodika v rámci svazku

2

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

6

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—