EFFECT OF Mn-ADDITION ON MICROSTRUCTURE, THERMAL AND MECHANICAL PROPERTIES OF CAST Al-Sc-Zr-BASED ALLOYS
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F11%3A10105326" target="_blank" >RIV/00216208:11320/11:10105326 - isvavai.cz</a>
Výsledek na webu
<a href="http://www.metal2011.com/data/metal2011/sbornik/lists/papers/729.pdf" target="_blank" >http://www.metal2011.com/data/metal2011/sbornik/lists/papers/729.pdf</a>
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
EFFECT OF Mn-ADDITION ON MICROSTRUCTURE, THERMAL AND MECHANICAL PROPERTIES OF CAST Al-Sc-Zr-BASED ALLOYS
Popis výsledku v původním jazyce
The effect of Mn content on microstructure, thermal and mechanical properties of cast Al-Sc-Zr alloy during isochronal annealing was studied. Specimens of three as-cast Al-Sc-based alloys with a various content of Mn and Zr were annealed up to ~ 570 oC.Precipitation reaction was studied by elec trical resistometry, microhardness (HV0.3) and differential scanning calorimetry measurements. The microstructure development was investigated by transmission electron microscopy and electron diffraction. The distinct microhardness increase observed after annealing above 270 oC corresponds excellently to the fastest resistivity changes as well as the heat flow changes. These changes are due to the precipitation of the Al3Sc particles. The apparent activation energy for precipitation of Al3Sc particles was determined. The phases of the Al-Sc-Zr system and also of the Al-Mn system were observed.
Název v anglickém jazyce
EFFECT OF Mn-ADDITION ON MICROSTRUCTURE, THERMAL AND MECHANICAL PROPERTIES OF CAST Al-Sc-Zr-BASED ALLOYS
Popis výsledku anglicky
The effect of Mn content on microstructure, thermal and mechanical properties of cast Al-Sc-Zr alloy during isochronal annealing was studied. Specimens of three as-cast Al-Sc-based alloys with a various content of Mn and Zr were annealed up to ~ 570 oC.Precipitation reaction was studied by elec trical resistometry, microhardness (HV0.3) and differential scanning calorimetry measurements. The microstructure development was investigated by transmission electron microscopy and electron diffraction. The distinct microhardness increase observed after annealing above 270 oC corresponds excellently to the fastest resistivity changes as well as the heat flow changes. These changes are due to the precipitation of the Al3Sc particles. The apparent activation energy for precipitation of Al3Sc particles was determined. The phases of the Al-Sc-Zr system and also of the Al-Mn system were observed.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2011
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Conference Proceedings Metal 2011
ISBN
978-80-87294-24-6
ISSN
—
e-ISSN
—
Počet stran výsledku
7
Strana od-do
872-878
Název nakladatele
Tanger Ltd.
Místo vydání
Ostrava
Místo konání akce
Brno
Datum konání akce
18. 5. 2010
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—