Internal stress and thermally activated dislocation motion in an AZ63 magnesium alloy

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F11%3A10107752" target="_blank" >RIV/00216208:11320/11:10107752 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.matchemphys.2011.08.045" target="_blank" >http://dx.doi.org/10.1016/j.matchemphys.2011.08.045</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.matchemphys.2011.08.045" target="_blank" >10.1016/j.matchemphys.2011.08.045</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Internal stress and thermally activated dislocation motion in an AZ63 magnesium alloy

Popis výsledku v původním jazyce

Magnesium alloy AZ63 was deformed at temperatures between room temperature and 300 degrees C. Stress relaxation tests were performed in order to reveal the physical base of the deformation process/-es. Internal and effective components of the applied stress have been estimated. Very high values of the internal stress estimated at room temperature decrease rapidly with increasing deformation temperature. The apparent activation volume decreases with increasing effective stress. Estimated values of the activation volume as well as the activation enthalpy indicate that the main thermally activated process is connected with the rapid decrease of the internal stress. (C) 2011 Elsevier B.V. All rights reserved.

Název v anglickém jazyce

Internal stress and thermally activated dislocation motion in an AZ63 magnesium alloy

Popis výsledku anglicky

Magnesium alloy AZ63 was deformed at temperatures between room temperature and 300 degrees C. Stress relaxation tests were performed in order to reveal the physical base of the deformation process/-es. Internal and effective components of the applied stress have been estimated. Very high values of the internal stress estimated at room temperature decrease rapidly with increasing deformation temperature. The apparent activation volume decreases with increasing effective stress. Estimated values of the activation volume as well as the activation enthalpy indicate that the main thermally activated process is connected with the rapid decrease of the internal stress. (C) 2011 Elsevier B.V. All rights reserved.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F09%2F0712" target="_blank" >GA106/09/0712: Vliv mikrostrukturních parametrů na aktivitu dvojčatění v hexagonálních kovech</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materials Chemistry and Physics

ISSN

0254-0584

e-ISSN

—

Svazek periodika

130

Číslo periodika v rámci svazku

3

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

5

Strana od-do

1146-1150

Kód UT WoS článku

000296830500049

EID výsledku v databázi Scopus

—