The effect of microstructure on fatigue performance of Ti-6Al-4V alloy after EDM surface treatment for application in orthopaedics
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F11%3A10108618" target="_blank" >RIV/00216208:11320/11:10108618 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1016/j.jmbbm.2011.06.012" target="_blank" >http://dx.doi.org/10.1016/j.jmbbm.2011.06.012</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.jmbbm.2011.06.012" target="_blank" >10.1016/j.jmbbm.2011.06.012</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
The effect of microstructure on fatigue performance of Ti-6Al-4V alloy after EDM surface treatment for application in orthopaedics
Popis výsledku v původním jazyce
Three different microstructures - equiaxed, bi-modal and coarse lamellar - are prepared from Ti-6Al-4V alloy. Electric discharge machining (EDM) with a high peak current (29 A) is performed in order to impose surface roughness and modify the chemical composition of the surface. Detailed scanning electron microscopy (SEM) investigation revealed a martensitic surface layer and subsurface heat affected zone (HAZ). EDX measurements showed carbon enriched remnants of the EDM process on the material surface.Rotating bending fatigue tests are undertaken for EDM processed samples for all three microstructures and also for electropolished - benchmark - samples. The fatigue performance is found to be rather poor and not particularly dependent on microstructure.The bi-modal microstructure shows a slightly superior high cycle fatigue performance. This performance can be further improved by a suitable heat treatment to an endurance limit of 200 MPa.
Název v anglickém jazyce
The effect of microstructure on fatigue performance of Ti-6Al-4V alloy after EDM surface treatment for application in orthopaedics
Popis výsledku anglicky
Three different microstructures - equiaxed, bi-modal and coarse lamellar - are prepared from Ti-6Al-4V alloy. Electric discharge machining (EDM) with a high peak current (29 A) is performed in order to impose surface roughness and modify the chemical composition of the surface. Detailed scanning electron microscopy (SEM) investigation revealed a martensitic surface layer and subsurface heat affected zone (HAZ). EDX measurements showed carbon enriched remnants of the EDM process on the material surface.Rotating bending fatigue tests are undertaken for EDM processed samples for all three microstructures and also for electropolished - benchmark - samples. The fatigue performance is found to be rather poor and not particularly dependent on microstructure.The bi-modal microstructure shows a slightly superior high cycle fatigue performance. This performance can be further improved by a suitable heat treatment to an endurance limit of 200 MPa.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2011
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of the Mechanical Behavior of Biomedical Materials
ISSN
1751-6161
e-ISSN
—
Svazek periodika
4
Číslo periodika v rámci svazku
—
Stát vydavatele periodika
NL - Nizozemsko
Počet stran výsledku
8
Strana od-do
1955-1962
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—