INVESTIGATION OF MICROHARDNESS AND MICROSTRUCTURE OF AZ31 ALLOY AFTER HIGH PRESSURE TORSION

Identifikátory výsledku

Alternativní jazyky

  • Jazyk výsledku

    angličtina

  • Název v původním jazyce

    INVESTIGATION OF MICROHARDNESS AND MICROSTRUCTURE OF AZ31 ALLOY AFTER HIGH PRESSURE TORSION

  • Popis výsledku v původním jazyce

    Cast commercial magnesium alloy AZ31 was processed by high pressure torsion (HPT) at room temperature for 1, 3, 5 and 15 rotations (strain ranged from 1 to 7). Microstructure evolution with strain imposed by HPT was observed by light and electron microscopy. HPT was shown to be a very effective method of grain refinement. The initial coarse grain structure was refined by a factor of almost 200 already after one HPT turn (? ALMOST EQUAL TO 4). Mechanical properties were investigated by detailed 2-D microhardness measurements. HPT straining was found to introduce a radial inhomogeneity in the material which is manifested by a pronounced drop in the center and the maximum near the specimen periphery. With increasing strain due to HPT this inhomogeneity iscontinuously smeared out tending to saturate with increasing strain. Integrated 3-D meshes across the total surface of disks revealed the undulating character of microhardness variations. The strain imposed by HPT was shown to saturate w

  • Název v anglickém jazyce

    INVESTIGATION OF MICROHARDNESS AND MICROSTRUCTURE OF AZ31 ALLOY AFTER HIGH PRESSURE TORSION

  • Popis výsledku anglicky

    Cast commercial magnesium alloy AZ31 was processed by high pressure torsion (HPT) at room temperature for 1, 3, 5 and 15 rotations (strain ranged from 1 to 7). Microstructure evolution with strain imposed by HPT was observed by light and electron microscopy. HPT was shown to be a very effective method of grain refinement. The initial coarse grain structure was refined by a factor of almost 200 already after one HPT turn (? ALMOST EQUAL TO 4). Mechanical properties were investigated by detailed 2-D microhardness measurements. HPT straining was found to introduce a radial inhomogeneity in the material which is manifested by a pronounced drop in the center and the maximum near the specimen periphery. With increasing strain due to HPT this inhomogeneity iscontinuously smeared out tending to saturate with increasing strain. Integrated 3-D meshes across the total surface of disks revealed the undulating character of microhardness variations. The strain imposed by HPT was shown to saturate w

Klasifikace

  • Druh

    D - Stať ve sborníku

  • CEP obor

    BM - Fyzika pevných látek a magnetismus

  • OECD FORD obor

Návaznosti výsledku

Ostatní

  • Rok uplatnění

    2011

  • Kód důvěrnosti údajů

    S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Údaje specifické pro druh výsledku

  • Název statě ve sborníku

    Magnesium Technology 2011

  • ISBN

    978-1-118-02936-7

  • ISSN

  • e-ISSN

  • Počet stran výsledku

    5

  • Strana od-do

    589-593

  • Název nakladatele

    Wiley

  • Místo vydání

    Neuveden

  • Místo konání akce

    San Diego

  • Datum konání akce

    27. 2. 2011

  • Typ akce podle státní příslušnosti

    WRD - Celosvětová akce

  • Kód UT WoS článku