Magnetocaloric effect of Gd64Co26Al9Y1 metallic glass
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F12%3A10126325" target="_blank" >RIV/00216208:11320/12:10126325 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/68378271:_____/12:00435251
Výsledek na webu
<a href="http://dx.doi.org/10.1016/j.jallcom.2012.07.137" target="_blank" >http://dx.doi.org/10.1016/j.jallcom.2012.07.137</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.jallcom.2012.07.137" target="_blank" >10.1016/j.jallcom.2012.07.137</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Magnetocaloric effect of Gd64Co26Al9Y1 metallic glass
Popis výsledku v původním jazyce
The samples of Gd64Co26Al9Y1 metallic glass were prepared by splat technique from the high purity elements. The glassy state of the samples was confirmed by the X-ray analysis. Their ferromagnetic ordering with the Curie temperature T-C = 108 K was identified from temperature dependence of magnetization and confirmed by AC-susceptibility measurement. Electrical conductivity of the glass increases with increasing temperature and exhibits a pronounced peak at T-C. The magnetocaloric effect was studied byheat capacity and magnetization isotherms measurements. Magnetic entropy change Delta S = -9.3 J kg(-1) K-1 was derived for a field span of 5 T. The adiabatic temperature change was measured directly in a field span of 4.7 T. (C) 2012 Elsevier B. V. Allrights reserved.
Název v anglickém jazyce
Magnetocaloric effect of Gd64Co26Al9Y1 metallic glass
Popis výsledku anglicky
The samples of Gd64Co26Al9Y1 metallic glass were prepared by splat technique from the high purity elements. The glassy state of the samples was confirmed by the X-ray analysis. Their ferromagnetic ordering with the Curie temperature T-C = 108 K was identified from temperature dependence of magnetization and confirmed by AC-susceptibility measurement. Electrical conductivity of the glass increases with increasing temperature and exhibits a pronounced peak at T-C. The magnetocaloric effect was studied byheat capacity and magnetization isotherms measurements. Magnetic entropy change Delta S = -9.3 J kg(-1) K-1 was derived for a field span of 5 T. The adiabatic temperature change was measured directly in a field span of 4.7 T. (C) 2012 Elsevier B. V. Allrights reserved.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2012
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of Alloys and Compounds
ISSN
0925-8388
e-ISSN
—
Svazek periodika
545
Číslo periodika v rámci svazku
srpen
Stát vydavatele periodika
NL - Nizozemsko
Počet stran výsledku
4
Strana od-do
1-4
Kód UT WoS článku
000311501800001
EID výsledku v databázi Scopus
—