Temperature deformation of the AX41 composites studied by the dilatometer measurements

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F12%3A10128507" target="_blank" >RIV/00216208:11320/12:10128507 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Temperature deformation of the AX41 composites studied by the dilatometer measurements

Popis výsledku v původním jazyce

Magnesium alloy AX41 reinforced with 15 vol. % of short saffil fibres and AX41 hybrid composite with 5 vol.% of saffil fibres and 15 vol.% of SiC particles were used in this study. Thermal expansion was measured over a wide temperature range (295 K - 673K). The thermal expansion coefficient was estimated during heating and cooling. The Young's modulus of the fibre composite was estimated and the modulus defect was compared with the relative change of the CTE. Dilatation characteristics of the pre-deformed hybrid composite were determined in the same temperature range as in the case of the fibre composite.

Název v anglickém jazyce

Temperature deformation of the AX41 composites studied by the dilatometer measurements

Popis výsledku anglicky

Magnesium alloy AX41 reinforced with 15 vol. % of short saffil fibres and AX41 hybrid composite with 5 vol.% of saffil fibres and 15 vol.% of SiC particles were used in this study. Thermal expansion was measured over a wide temperature range (295 K - 673K). The thermal expansion coefficient was estimated during heating and cooling. The Young's modulus of the fibre composite was estimated and the modulus defect was compared with the relative change of the CTE. Dilatation characteristics of the pre-deformed hybrid composite were determined in the same temperature range as in the case of the fibre composite.

Druh

D - Stať ve sborníku

CEP obor

JI - Kompositní materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GCP108%2F12%2FJ018" target="_blank" >GCP108/12/J018: Zpevnění a odpevnění v deformovaných kompozitech na bázi hořčíku</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Proceedings of the 15th European Conference on Composite Materials

ISBN

978-88-88785-33-2

ISSN

—

e-ISSN

—

Počet stran výsledku

8

Strana od-do

—

Název nakladatele

Department of Management and Engineering University of Padova

Místo vydání

Padova, Itálie

Místo konání akce

Benátky, Itálie

Datum konání akce

24. 6. 2012

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—