The effect of Zr addition on the structure and high temperature strength of Fe-30 at.% Al type alloys

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F12%3A10130262" target="_blank" >RIV/00216208:11320/12:10130262 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/46747885:24210/12:#0002785

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.intermet.2011.08.007" target="_blank" >http://dx.doi.org/10.1016/j.intermet.2011.08.007</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.intermet.2011.08.007" target="_blank" >10.1016/j.intermet.2011.08.007</a>

Jazyk výsledku

angličtina

Název v původním jazyce

The effect of Zr addition on the structure and high temperature strength of Fe-30 at.% Al type alloys

Popis výsledku v původním jazyce

The structure of four Fe-30Al alloys with different contents of Zr has been studied. Light optical microscopy (LOM), scanning electron microscopy (SEM) with EDX module, measurement of microhardness as well as X-ray diffraction (XRD) was used to determinethe structure and phase composition. Addition of Zr to Fe-30Al leads, in the cast state, to the formation of a Fe-Al matrix with a hard lamellar eutectic skeleton. The eutectic is composed of thin lamellae of lambda(1)-Laves phase Zr(Fe,Al)(2) and Fe-Al(B2/D0(3)). Annealing at 1000 degrees C for 200 h results in the formation of the equilibrium phase tau(1) Zr(Fe,Al)(12). The presence of these phases in the matrix leads to increase of high temperature yield stress and strength.

Název v anglickém jazyce

The effect of Zr addition on the structure and high temperature strength of Fe-30 at.% Al type alloys

Popis výsledku anglicky

The structure of four Fe-30Al alloys with different contents of Zr has been studied. Light optical microscopy (LOM), scanning electron microscopy (SEM) with EDX module, measurement of microhardness as well as X-ray diffraction (XRD) was used to determinethe structure and phase composition. Addition of Zr to Fe-30Al leads, in the cast state, to the formation of a Fe-Al matrix with a hard lamellar eutectic skeleton. The eutectic is composed of thin lamellae of lambda(1)-Laves phase Zr(Fe,Al)(2) and Fe-Al(B2/D0(3)). Annealing at 1000 degrees C for 200 h results in the formation of the equilibrium phase tau(1) Zr(Fe,Al)(12). The presence of these phases in the matrix leads to increase of high temperature yield stress and strength.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F08%2F1238" target="_blank" >GA106/08/1238: Studium možností zpevnění slitin na bázi aluminidů železa částicemi sekundárních fází</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Intermetallics

ISSN

0966-9795

e-ISSN

—

Svazek periodika

20

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

8

Strana od-do

39-46

Kód UT WoS článku

000297889300006

EID výsledku v databázi Scopus

—