Natural aging of Mg-Gd and Mg-Tb alloys
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F12%3A10131298" target="_blank" >RIV/00216208:11320/12:10131298 - isvavai.cz</a>
Výsledek na webu
<a href="http://onlinelibrary.wiley.com/doi/10.1002/pssa.201228327/abstract;jsessionid=59754F3EFE1613E06344C40D7C6C3FC0.d04t03" target="_blank" >http://onlinelibrary.wiley.com/doi/10.1002/pssa.201228327/abstract;jsessionid=59754F3EFE1613E06344C40D7C6C3FC0.d04t03</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1002/pssa.201228327" target="_blank" >10.1002/pssa.201228327</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Natural aging of Mg-Gd and Mg-Tb alloys
Popis výsledku v původním jazyce
Substantial natural aging occurring on the time scale of less than 1 month was observed in solution-treated Mg-Gd and Mg-Tb alloys. Solution treatment at 500 and 530 8C for Mg-Gd and Mg-Tb alloys, respectively, leads to dissolution of Gd or Tb in the Mgmatrix. By quenching of solution-treated alloys to room temperature a supersaturated solid solution of Gd or Tb in Mg was formed. During subsequent aging at ambient temperature the hardness of quenched alloys increases, most probably, due to agglomeration of dissolved Gd or Tb atoms into small clusters. Positron lifetime spectroscopy combined with coincident Doppler broadening revealed that quenched alloys contain vacancies bound to Gd or Tb atoms. Quenched-in vacancies facilitate clustering of Gd or Tbsolutes and disappear from the samples when the clusters are fully developed.
Název v anglickém jazyce
Natural aging of Mg-Gd and Mg-Tb alloys
Popis výsledku anglicky
Substantial natural aging occurring on the time scale of less than 1 month was observed in solution-treated Mg-Gd and Mg-Tb alloys. Solution treatment at 500 and 530 8C for Mg-Gd and Mg-Tb alloys, respectively, leads to dissolution of Gd or Tb in the Mgmatrix. By quenching of solution-treated alloys to room temperature a supersaturated solid solution of Gd or Tb in Mg was formed. During subsequent aging at ambient temperature the hardness of quenched alloys increases, most probably, due to agglomeration of dissolved Gd or Tb atoms into small clusters. Positron lifetime spectroscopy combined with coincident Doppler broadening revealed that quenched alloys contain vacancies bound to Gd or Tb atoms. Quenched-in vacancies facilitate clustering of Gd or Tbsolutes and disappear from the samples when the clusters are fully developed.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2012
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Physica Status Solidi (A) Applications and Materials
ISSN
1862-6300
e-ISSN
—
Svazek periodika
209
Číslo periodika v rámci svazku
11
Stát vydavatele periodika
DE - Spolková republika Německo
Počet stran výsledku
7
Strana od-do
2135-2141
Kód UT WoS článku
000313729800006
EID výsledku v databázi Scopus
—