Microstructure and Mechanical Properties of the Cold-Rolled Al-Mn and Al-Mn-Sc-Zr Alloys
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F13%3A10189001" target="_blank" >RIV/00216208:11320/13:10189001 - isvavai.cz</a>
Výsledek na webu
<a href="http://www.metal2014.com/files/uploads/02/Proceedings_METAL2013_Content.pdf" target="_blank" >http://www.metal2014.com/files/uploads/02/Proceedings_METAL2013_Content.pdf</a>
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Microstructure and Mechanical Properties of the Cold-Rolled Al-Mn and Al-Mn-Sc-Zr Alloys
Popis výsledku v původním jazyce
The conference paper reports results of a study aimed at understanding precipitation processes of the binary Al-Mn and quaternary Al-Mn-Sc-Zr alloy. The alloys were investigated in the mould-cast state and coldrolled state. The alloys were studied duringstep-by-step quasilinear annealing from 200 oC up to 600 oC with heating rate 100 K/h followed by subsequent isothermal annealing at 600 oC/4 h. The effect of the pseudohomogenization heat treatment (610 oC/18 h) on mechanical properties of the alloys during isothermal annealing at 300, 400 and 500 oC was also investigated. Precipitation reactions were studied by electrical resistometry and (micro)hardness measurements. The microstructure development was investigated by transmission, scanning electronmicroscopy and electron diffraction examinations. The hardening effect is due to fine, coherent, uniformly distributed Al3Sc and/or Al3(Sc,Zr) particles. The distinct changes in resistivity of the cold-rolled alloys at temperature above ~
Název v anglickém jazyce
Microstructure and Mechanical Properties of the Cold-Rolled Al-Mn and Al-Mn-Sc-Zr Alloys
Popis výsledku anglicky
The conference paper reports results of a study aimed at understanding precipitation processes of the binary Al-Mn and quaternary Al-Mn-Sc-Zr alloy. The alloys were investigated in the mould-cast state and coldrolled state. The alloys were studied duringstep-by-step quasilinear annealing from 200 oC up to 600 oC with heating rate 100 K/h followed by subsequent isothermal annealing at 600 oC/4 h. The effect of the pseudohomogenization heat treatment (610 oC/18 h) on mechanical properties of the alloys during isothermal annealing at 300, 400 and 500 oC was also investigated. Precipitation reactions were studied by electrical resistometry and (micro)hardness measurements. The microstructure development was investigated by transmission, scanning electronmicroscopy and electron diffraction examinations. The hardening effect is due to fine, coherent, uniformly distributed Al3Sc and/or Al3(Sc,Zr) particles. The distinct changes in resistivity of the cold-rolled alloys at temperature above ~
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GPP107%2F11%2FP201" target="_blank" >GPP107/11/P201: Využití precipitace a rekrystalizace při přípravě Al slitin s požadovanými vlastnostmi</a><br>
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2013
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
METAL 2013 Conference Proceedings
ISBN
978-80-87294-41-3
ISSN
—
e-ISSN
—
Počet stran výsledku
6
Strana od-do
1224-1229
Název nakladatele
Tanger Ltd.
Místo vydání
Ostrava
Místo konání akce
Brno
Datum konání akce
15. 5. 2013
Typ akce podle státní příslušnosti
EUR - Evropská akce
Kód UT WoS článku
—