Inhibition of Positronium Formation in Yttria Stabilized Zirconia Nanopowders Modified by Addition of Chromia
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F13%3A10189622" target="_blank" >RIV/00216208:11320/13:10189622 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.4028/www.scientific.net/MSF.733.249" target="_blank" >http://dx.doi.org/10.4028/www.scientific.net/MSF.733.249</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.4028/www.scientific.net/MSF.733.249" target="_blank" >10.4028/www.scientific.net/MSF.733.249</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Inhibition of Positronium Formation in Yttria Stabilized Zirconia Nanopowders Modified by Addition of Chromia
Popis výsledku v původním jazyce
The effect of chromia additive on defects in yttria stabilized zirconia (YSZ) nanopowders was investigated in this work. It was found that positrons are trapped at vacancy-like misfit defects at grain boundaries and at larger defects situated at triple points. Moreover, a long-lived ortho-positronium contribution was found in YSZ nanopowder without chromia. Addition of chromia prolongs the lifetime of positrons trapped at vacancy-like misfit defects which indicates segregation of Cr ions at grain interfaces and interaction of Cr with vacancy-like misfit defects. Furthermore, addition of chromia completely suppresses formation of positronium.
Název v anglickém jazyce
Inhibition of Positronium Formation in Yttria Stabilized Zirconia Nanopowders Modified by Addition of Chromia
Popis výsledku anglicky
The effect of chromia additive on defects in yttria stabilized zirconia (YSZ) nanopowders was investigated in this work. It was found that positrons are trapped at vacancy-like misfit defects at grain boundaries and at larger defects situated at triple points. Moreover, a long-lived ortho-positronium contribution was found in YSZ nanopowder without chromia. Addition of chromia prolongs the lifetime of positrons trapped at vacancy-like misfit defects which indicates segregation of Cr ions at grain interfaces and interaction of Cr with vacancy-like misfit defects. Furthermore, addition of chromia completely suppresses formation of positronium.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JH - Keramika, žáruvzdorné materiály a skla
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2013
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Materials Science Forum
ISBN
—
ISSN
0255-5476
e-ISSN
—
Počet stran výsledku
5
Strana od-do
249-253
Název nakladatele
TRANS TECH PUBLICATIONS LTD
Místo vydání
STAFA-ZURICH
Místo konání akce
Smolenice
Datum konání akce
5. 9. 2011
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
000315535700052